Efeito da relação siringil/guaiacil e de fenóis derivados da lignina nas características da madeira e do carvão vegetal de Eucalyptus spp

Caxito de Araújo Ana Clara, Trugilho Paulo Fernando, Napoli Alfredo, de Carvalho Braga Pedro Paulo, de Lima Rafaeli Valério, Protásio Thiago de Paula. 2016. Efeito da relação siringil/guaiacil e de fenóis derivados da lignina nas características da madeira e do carvão vegetal de Eucalyptus spp. Scientia Forestalis, 44 (110) : 405-414.

https://doi.org/10.18671/scifor.v44n110.13

Article de revue ; Article de revue à facteur d'impact

Version publiée - Portugais
Accès réservé aux personnels Cirad
Utilisation soumise à autorisation de l'auteur ou du Cirad.
cap13.pdf
Télécharger (783kB) | Demander une copie

Titre anglais : Effects of the syringyl/guaiacyl ratio and of lignin-derived phenols on the wood and charcoal characteristics in Eucalyptus spp

Quartile : Q4, Sujet : FORESTRY

Résumé : Este estudo teve como objetivo determinar a relação existente entre os conteúdos dos fenóis siringaldeído (Sg) e vanilina (V), derivados de lignina, e a relação siringil/guaiacil com as características da madeira, do carvão vegetal bem como com a perda de massa durante a pirólise. O experimento foi conduzido com sete materiais genéticos de Eucalyptus, e os dados avaliados por meio da análise de correlação de Pear¬son. Observou-se correlações significativas do conteúdo de vanilina, siringaldeído e relação S/G com as características avaliadas na madeira, no carvão vegetal e com a perda de massa durante a pirólise. Tanto o conteúdo de vanilina como o de siringaldeído, apresentou correlação significativa com o rendimento gravimétrico da carbonização. A amostra com maior quantidade de vanilina apresentou menor perda de massa entre 315-390ºC (48,10%) ocasionando maior massa residual aos 450ºC (22,40%). A correlação observada entre o teor de vanilina e a perda de massa neste intervalo de temperatura evidencia o potencial das estruturas guaiacílicas da lignina para elevar o rendimento gravimétrico em carvão vegetal.

Résumé (autre langue) : This study aimed to determine the relationship between the contents of phenols syringaldehyde (Sg) and vanillin (V), derived from lignin and syringyl / guaiacyl ratio (S/G) with the wood and charcoal characteristics, as well as the mass loss in the process of pyrolysis. The experiment was obtained with seven Eucalyptus taxa, and the data evaluated by Pearson correlation analysis. There were statistically significant correlations of the vanillin and syringaldehyde contents, and S / G ratio with the characteristics of the wood, charcoal and with the mass loss during pyrolysis process. Both the vanillin as the syringaldehyde contents showed a significant correlation with the gravimetric yield of carbonization. The sample with the highest amount of vanillin showed less weight loss between 315-390ºC (48.10%) resulting in higher residual mass at 450°C (22.40%). The correlation between the vanillin content and the weight loss at this temperature range shows the potential of guaiacyl lignin structures to elevate the gravimetric yield of charcoal.

Mots-clés Agrovoc : bois, Eucalyptus, charbon de bois, pyrolyse, gravimétrie, phénol, lignine, carbonisation du bois

Mots-clés géographiques Agrovoc : Minas Gerais

Classification Agris : K50 - Technologie des produits forestiers
P06 - Sources d'énergie renouvelable

Champ stratégique Cirad : Axe 2 (2014-2018) - Valorisation de la biomasse

Auteurs et affiliations